Heating a Slab & Levelling Compound

[Spinny]

So my last lot of floor levelling compound was put down 27 days ago and has been left to go off and dry naturally in that time. All be it chunks of the floor have had floor mats and kitchen parts all over them for a couple of weeks of that. Kitchen now sitting on legs awaiting parts.

 

Floor makeup - 120mm concrete slab with heating pipes around midpoint, approx 25mm to 5mm of levelling compound on top in 2 coats, top coat between 15mm and 3mm.

 

Time to run some heat through the slab, but it is June.

Unheated the surface of the levelling compound is around 24 today anyway - using my heat gun.

(Presumably temp is lower deeper within the slab ?)

I have turned down the flow temp to Min - probably about 25C ? ? - and just turned on the underfloor heating.

 

Advice please on how long to run it and how to increment the water temperature over the days to come ?

(LVT to be laid in 26 days time)

Edited yesterday at 17:51 by Spinny

[JohnMo]

If your a well insulated house, your flow temp isn't going to much higher than about 28 at -lots outside, so zero point going beyond that. We never bothered doing any drying cycling as we didn't have a heat source at the time.

 

Your heat pump is pretty unlikely to fire up, if the floor is already warm. It will or should have a drying programme, so run that and limit max temperature otherwise you'll just melt.

[Spinny]

Ah. No heat pump, gas boiler.

There is a mixer valve on the manifold. I am not actually sure how accurate those things are but in the winter we had it set at 45C, albeit we still had no insulation around the bifolds. Boiler output is at 60C to rads. Floor temperature got up to 26C then.

 

I guess Min on the valve is perhaps equivalent to off ? i.e. cold water feed temperature ?

Tweaked it up a fraction, heat gun has pipes at 22C.

 

The concrete slab itself is well dried out, been heated through two winters.

Edited yesterday at 18:38 by Spinny

[Nickfromwales]

Just time the heating to do an hour on then 2 hrs off, then repeat. 

[Spinny]

Hmm. I have been doing something similar to what you suggest @Nickfromwales

I suspect that as the surface is around 22C, then it might well be that heating the slab to 22C (though it may not be getting to that) has no effect whatsoever on the levelling compound on top. Essentially the heating below is no different from the heating the levelling compound is receving from the environment above it.

I shall gradually increase the flow temperature over the coming days.

[Nickfromwales]

4 minutes ago, Spinny said:

Hmm. I have been doing something similar to what you suggest @Nickfromwales

I suspect that as the surface is around 22C, then it might well be that heating the slab to 22C (though it may not be getting to that) has no effect whatsoever on the levelling compound on top. Essentially the heating below is no different from the heating the levelling compound is receving from the environment above it.

I shall gradually increase the flow temperature over the coming days.

Don’t overheat it. Slow and steady wins the race.